FTIR, SEM/EDS and ion chromatography used in concert with a pair of extraction methods offered varying degrees of precision.

A group of 25 conformal-coated, no-clean assemblies was placed in an environmental test chamber at 40°C/90%RH for 168 hr. under functional conditions. Each assembly was tested with its plastic/metal enclosure on the unit; large openings in the enclosures permitted the assemblies to be exposed to the environmental conditions. Twenty-two units produced dendrites in multiple locations; all grew shorts on the SMT pad without components (FIGURE 1). The units were biased with 3.3V for 168 hr. at 40oC/90%RH.

foresite1
Figure 1. Dendrite on unit #414.

FTIR, SEM/EDS and IC (ion chromatography)1 methods using total board (bag) and C3 localized area extractions were performed to understand the dendrite failures per the client’s request. The localized extractions were performed at the specific area of the failure and a reference area.

FTIR (Fourier transform infrared spectroscopy) analysis was performed using a Thermo Nicolet iS10 spectrometer and Continuum Microscope. A match was shown to the reference area of the nearby conformal coating. Data interpretations of FTIR analysis (FIGURE 2) show that the dendrite area matches only the conformal coating reference residues.

foresite2
Figure 2. FTIR analysis of unit #414.

SEM/EDS  analysis was conducted in an Amray SEM/EDS system using variable pressure mode. This does not require gold or carbon coating of the specimen and
requires additional analysis to be performed after SEM/EDS on the same unit (#414).

EDS analysis (FIGURE 3) of unit #414 shows detectable elements as carbon, oxygen, silicon, (no chloride was detected with the markers on) and tin. SEM (FIGURE 4) and optical imaging (FIGURE 5) show dendrites grew on top of the conformal coating and not underneath. The SMT pads show no coating on the pad surface, permitting the metal to react with fluid on the surface of the PCBA. 

foresite3
Figure 3. EDS analysis of the dendrite on unit #414.

foresite4
Figure 4. SEM/EDS image of dendrites.

foresite5
Figure 5. Dendrite area on top of the conformal coating.

Ion chromatography analysis was performed using the C3 test and extraction system specific for site extractions. A reference area on top of the conformal coating was extracted, followed by the area under the coating where failures occurred.

After the C3 localized2 extractions were completed, the conformal coated board (total board) was bag extracted with 10% IPA/90% DI water for one hr. at 80°C. FIGURE 6 shows the C3 test cell on reference (coated) area of PCBA. FIGURE 7 shows the C3 test cell on dendrite location with coating and SMT pads exposed. Based on the results of the dendrite and reference areas, a third extraction location on the plastic housing (FIGURE 8) was chosen directly above the dendrite.

foresite6
Figure 6. C3 localized extraction of reference area.

foresite7
Figure 7. C3 localized extraction of dendrite area.

foresite8
Figure 8. Extraction location inside housing.

The reference area C3 results were “Clean,” indicating that the residue did not short the electrode in the C3 test cell during the 180 sec. run time (FIGURE 9). The test of the dendrite area read “Dirty,” indicating the copper electrode with a 10V bias shorted in 30 sec. at 250µA of current (FIGURE 10).

foresite9 
Figure 9. C3 results of reference area.

foresite10
Figure 10. C3 results of dendrite area.

The residues on the inside of the housing tested “Dirty” in less than 1 sec., shorting the copper traces in the solution (FIGURE 11).

foresite11
Figure 11. C3 results of housing area.

FIGURE 12 shows the C3 reference area on top of the coating, with exposed metal on the resistors’ surfaces. FIGURE 13 shows the dendrite area, where the top of the reflowed pad lacks complete coating coverage.

foresite12
Figure 12. Reference area on top of coating.

foresite13
Figure 13. Dendrite area on reflowed pads.

The plastic housing (Figure 8) above the dendrite area was tested to see if residues were transferring to the board surface. The anion residues identified by IC analysis in the reference area (FIGURE 14) showed low levels of acetate, chloride, sulfate and WOA. Residues detected from the isolated dendrite area (FIGURE 15) showed high levels of acetate, formate, chloride and sulfate that were not present in the reference area. Residues detected from inside the plastic surface (FIGURE 16) showed the highest levels of acetate, formate, chloride and sulfate. This residue signature is typical of a mold release for plastic parts.

foresite14
Figure 14. Reference area chromatogram.

foresite15

Figure 15. Dendrite area chromatogram.

forestire16
Figure 16. Plastic housing chromatogram.

A Thermo ICS 3000 IC using an anion column AS22 with a modified eluent isocratic bicarbonate/bicarb structure for optimal separation of ionic and organic residues and a CS12A column with a sulfuric acid eluent structure provided more accurate results from the C3 extractions. TABLE 1 shows that the total board, 100mls, bag extractions (using 90% DI water/10% IPA) of the PCBs with dendrites had relatively low levels of ionic and organic residues, compared to the localized C3 extractions.

Table 1. Ion Chromatography Results of Both C3 and Bag Extraction SamplescoverStoryTable

Conclusions

FTIR testing showed no difference organically on the surface of the dendrites from the coated reference area. No root cause for the failure could be determined by this analytical method for dendrite growth.

SEM and optical imaging showed the dendrite growth was on top of the coating and that the coating did not completely cover the solder mound, leaving the exposed metal to react within the environmental conditions. Optical imaging with UV light showed the exposed metallization of the solder domes was not covered by conformal coating. No root cause for the failure could be determined by this analytical method for dendrite growth, but it does show there is an open path for condensate to bridge pads.

EDS analysis showed the dendrites are comprised of tin, carbon and oxygen. There was not enough concentration to detect chlorine or sulfur elements. No root cause for the failure could be determined by this analytical method for dendrite growth.

Ion chromatography using total board extractions in a bag at 80°C for one hr. (board surface only) showed acceptable levels of acetate, chloride, sulfate, WOA, sodium and ammonium. This larger volume of 10% IPA/90% DI water (60mL per 48 in2) dilutes the sample to acceptable levels of ionic contamination. No root cause for the failure could be determined by this analytical method for dendrite growth.

Ion chromatography using C3 localized extractions comparing the dendrite area to the reference area led us to analyze the molded plastic housing above the dendrite area. C3 results of the dendrite showed “Dirty” C3 results in 30 sec. and good “Clean” results of the reference area with the same exposed solder pad domes. C3 analysis of the plastic housing, above the shorting location, showed C3 results as “Dirty” with a failure time of 0.2 sec., causing a short to bridge the C3 electrode with 10V. IC results for the dendrite and inside housing locations showed high acetate, chloride, sulfate, sodium and ammonium residues not present on the reference area. This is a typical residue signature for many of the mold release and mold protection systems found on plastic housings and enclosures that can be transferred during heat and humidity testing of electronics systems. Using localized extraction, it was determined the board processing was clean, and contamination from the housing was responsible for dendrite shorting of the powered devices.

Root cause for the failure was the housing cleanliness prior to assembly. Residues were transferred during elevated humidity testing, leaving micro drops of corrosive fluid on the surface of the coated, assembled PCB surface. This permitted the dendrite to form on the surface of the coating.

References

1. IPC-TM-650, Test Methods Manual, test method 2.3.28B, “Ionic Analysis of Circuit Boards, Ion Chromatography,” November 2012.
2. Stephen Shoda and Terry Munson, “Cleanliness Evaluation for Electronic Hardware Reliability,” IPC Apex Proceedings, February 2007.

Ed.: This article was first presented at SMTA International in October 2014 and is published here with permission of the author.

Terry Munson is founder and president of Foresite (foresiteinc.com); terrym@residues.com.

Submit to FacebookSubmit to Google PlusSubmit to TwitterSubmit to LinkedInPrint Article
Mike Buetow

CAVEAT LECTOR

Lots of talk about machine communication.
Mike Buetow
Peter Bigelow

ROI

Multisite management.

Peter Bigelow
Susan Mucha

FOCUS ON BUSINESS

Multisite management.
Susan Mucha
Clive Ashmore

SCREEN PRINTING

Understencil cleaning.

Clive Ashmore
John Borneman 

GETTING LEAN

Are you capable?

John Borneman
Martin Wickham

DEFECTS DATABASE

Feeling crimped.

Martin Wickham